優勢說明:PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3詳細說明:
1.PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3
: 本公司可以免費提供各種材料認證
產品說明 | |
Vydyne® 55HSP BK is a heat stabilized molding grade Nylon 66 resin available in natural color and black. It is lubricated for improved machine feed and mold release and is intended for use in applications requiring fast molding cycles and outstanding mold release performance. The stabilization package has been formulated to provide improved retention of physical and electrical properties, compared to non-heat stabilized grades during long term exposure to high temperatures. Vydyne 22HSP Series offer a well balanced combination of engineering properties characterized by high strength, rigidity, good toughness in use, high melting point, good surface lubricity, and abrasion resistance. In addition, it is resistant to many chemicals and solvents, including gasoline, and machine and motor oils. Internally and externally lubricated for improved machine feed and exceptional mold release. Vydyne 22HSP Series are intended for use in high productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where Vydyne 22HSP Series resins can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing (English)Technical Datasheet (English) |
UL 黃卡 2 | E70062-249060E70062-101446500 |
搜索 UL 黃卡 | Ascend Performance Materials LLC.Vydyne® |
供貨地區 | 北美洲歐洲亞太地區 |
添加劑 | 熱穩定劑潤滑劑 |
性能特點 | 熱穩定 耐高溫 高韌性 黑色 增韌剛性,高高強度經潤滑抗溶解性耐化學性良好耐磨蝕性,良好耐汽油性耐油性能熱穩定性韌性良好生產階段,快脫模性能良好 |
用途 | 墊圈閥門/閥門部件工業領域:緊固件連接器汽車領域的應用:套管凸輪軸承 |
機構評級 | ASTM D 4066 PA0121ASTM D 6779 PA02121FED L-P-410AMIL M-20693B |
RoHS 合規性 | RoHS 合規 |
UL 檔案號 | E70062 |
外觀 | 黑色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
多點數據 | Isothermal Stress vs. Strain (ISO 11403-1) |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.14 | -- | g/cm3 | ISO 1183 |
收縮率 | ISO 294-4 | |||
橫向流量: 73°F, 0.0787 in | 1.6 | -- | % | |
流量: 73°F, 0.0787 in | 1.4 | -- | % | |
吸水率 | ISO 62 | |||
73°F, 24 hr | 1.1 | -- | % | |
平衡, 73°F, 50% RH | 2.4 | -- | % |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 435000 | 203000 | psi | ISO 527-2 |
拉伸應力 (屈服, 73°F) | 12000 | 9570 | psi | ISO 527-2 |
拉伸應變 | ISO 527-2 | |||
屈服, 73°F | 4.5 | 25 | % | |
斷裂, 73°F | 25 | 110 | % | |
彎曲模量 (73°F) | 421000 | 196000 | psi | ISO 178 |
彎曲強度 (73°F) | 12500 | 3190 | psi | ISO 178 |
泊松比 | 0.41 | -- | ISO 527-2 | |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 2.5 | -- | ft·lb/in2 | |
73°F | 3.1 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 無斷裂 | -- | ||
73°F | 無斷裂 | -- | ||
懸壁梁缺口沖擊強度 (73°F) | 2.6 | -- | ft·lb/in2 | ISO 180 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 392 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 158 | -- | °F | ISO 75-2/A |
維卡軟化溫度 | 457 | -- | °F | ISO 306/B |
溶融溫度(DSC) | 500 | -- | °F | ISO 3146 |
線形膨脹系數 | ISO 11359-2 | |||
流動: 73 到 131°F, 0.0787 in | 6.1E-6 | -- | in/in/°F | |
橫向: 73 到 131°F, 0.0787 in | 6.7E-6 | -- | in/in/°F | |
RTI Elec | UL 746 | |||
0.0280 in | 284 | -- | °F | |
0.0591 in | 284 | -- | °F | |
0.118 in | 284 | -- | °F | |
RTI Imp | UL 746 | |||
0.0280 in | 203 | -- | °F | |
0.0591 in | 230 | -- | °F | |
0.118 in | 230 | -- | °F | |
RTI Str | UL 746 | |||
0.0280 in | 239 | -- | °F | |
0.0591 in | 257 | -- | °F | |
0.118 in | 257 | -- | °F |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 (0.118 in) | 4.0E+15 | -- | ohm·cm | IEC 60093 |
耐電強度 3 (73°F, 0.118 in) | 510 | -- | V/mil | IEC 60243-1 |
耐電弧性 (0.118 in) | PLC 6 | -- | ASTM D495 | |
相比耐漏電起痕指數(CTI) (0.118 in) | PLC 1 | -- | UL 746 | |
漏電起痕指數 (0.118 in) | 400 到 599 | -- | V | IEC 60112 |
高電弧燃燒指數(HAI) | UL 746 | |||
0.0280 in | PLC 0 | -- | ||
0.0591 in | PLC 0 | -- | ||
0.118 in | PLC 0 | -- | ||
高電壓電弧起痕速率 (HVTR) (0.118 in) | PLC 0 | -- | UL 746 | |
熱絲引燃 (HWI) | UL 746 | |||
0.0280 in | PLC 4 | -- | ||
0.0591 in | PLC 4 | -- | ||
0.118 in | PLC 4 | -- | ||
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
UL 阻燃等級 | UL 94 | |||
0.0280 in, All colors | V-2 | -- | ||
0.0591 in, All colors | V-2 | -- | ||
0.118 in, All colors | V-2 | -- | ||
灼熱絲易燃指數 | IEC 60695-2-12 | |||
0.0280 in | 1520 | -- | °F | |
0.0591 in | 1520 | -- | °F | |
0.118 in | 1760 | -- | °F | |
熱燈絲點火溫度 | IEC 60695-2-13 | |||
0.0280 in | 1290 | -- | °F | |
0.0591 in | 1290 | -- | °F | |
0.118 in | 1290 | -- | °F |
注射 | 干燥 | 單位制 | |
干燥溫度 | < 158 | °F | |
干燥時間 | 1.0 到 3.0 | hr | |
建議注入量 | 40 到 80 | % | |
建議的zui大回制料比例 | 25 | % | |
螺筒后部溫度 | 518 到 590 | °F | |
螺筒中部溫度 | 518 到 590 | °F | |
螺筒前部溫度 | 518 到 590 | °F | |
射嘴溫度 | 518 到 590 | °F | |
加工(熔體)溫度 | 527 到 581 | °F | |
模具溫度 | 59.0 到 203 | °F | |
注塑溫度 | 7980 到 20300 | psi | |
注射速度 | 快速 | ||
保壓 | 7980 到 20300 | psi | |
背壓 | 29.0 到 145 | psi | |
螺桿轉速 | 50 到 150 | rpm | |
合模力 | 1.9 到 4.5 | tons/in2 | |
墊層 | 0.118 到 0.252 | in | |
注射說明 | |||
Injection Time: <1 to 2.5 sec |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
現貨PA66美國首諾 55HSP BK 熱穩定 耐高溫 高韌性 黑色 增韌其它產品
現貨PA66美國首諾 55HSP BK 熱穩定 耐高溫 高韌性 黑色 增韌
現貨PA66美國首諾 55HSP BK 汽車應用:卡扣 套管 凸輪 軸承
PA66美國首諾 41LDC 剛性,高剛性,良好經潤滑
PA66美國首諾 20NSP工業領域: 緊固件 連接器
PA66美國首諾 20NSP NC工業領域: 緊固件 連接器
PA66美國首諾 R543H 汽車的發動機罩下的零件
PA66美國首諾 R543H 尺草坪和園林設備 齒輪
PA66美國首諾 R543H 尺寸穩定性良好 剛性,高 高拉伸強度 高強
PA66美國首諾 R543H 耐汽油性 耐油性能 耐油脂性能 熱穩定性
PA66美國首諾 R543H 抗溶解性 抗撞擊性,良好