聚甲醛塑料,俗稱賽鋼,為結(jié)晶性熱可塑性塑料,具明顯熔點(diǎn)165~175℃,性質(zhì)zui接近金屬。
產(chǎn)品說明 | |
Rapidly solidifying standard grade for injection molding. Abbreviated designation according to ISO 1043: POM Designation according to ISO 9988-1: POM-K, M-GNR, 03-002 Ultraform® is supplied in the form of granules having a bulk density of approx. 850 g/l. Standards packs are the 25 kg PE bag and the 1000 kg Oktabin (octagonal container). Ultraform® is not subject to change when it is stored in dry, ventilated rooms. After relatively long storage (>1 year) or when handling material from previously opened containers, preliminary drying is recommended in order to remove any moisture which has been absorbed. Ultraform® is not a hazardous material as defined in the German Ordinance on Hazardous Materials. If Ultraform® is processed properly little or no formaldehyde occurs in the region of the processing machine. Measures should be taken to ensure ventilation and venting of the work area, preferably by means of an extraction hood over the barrel unit. Ultraform® decomposes when subjected to excessive heat. The decomposition products formed in this case consist almost exclusively of formaldehyde, a gas which has a pungent smell even at very low concentrations and irritates the mucous membranes. Decomposition can rapidly result in the build-up of a high gas pressure in the barrel of the processing unit. If the die is sealed there may be a sudden release of pressure via the filling hopper. Contamination of Ultraform® by thermoplastics that cause ecomposition of polyacetals, e.g. PVC or plastics containing halogenated fire protection agents, must be avoided under all circumstances. Even small quantities can cause uncontrolled and rapid decomposition of Ultraform® during processing. Pellets and finished parts must not be allowed to come into contact with strong acids (especially concentrated hydrochloric acid) since they cause Ultraform® to decompose. | |
總體 | |
材料狀態(tài) | 已商用:當(dāng)前有效 |
資料 1 | Processing - Injection Molding Cooling Times (English)Technical Datasheet (English) |
UL 黃卡 2 | E41871-233594 |
搜索 UL 黃卡 | BASF CorporationUltraform® |
供貨地區(qū) | 歐洲 |
性能特點(diǎn) | 一般目的 |
用途 | 一般目的 |
機(jī)構(gòu)評級 | EC 1907/2006 (REACH) |
形式 | 顆粒 |
加工方法 | 注射成型 |
樹脂ID (ISO 1043) | POM |
物理性能 | 額定值 | 單位制 | 測試方法 |
密度 | 1.40 | g/cm3 | ISO 1183 |
溶化體積流率(MVR) (190°C/2.16 kg) | 0.458 | in3/10min | ISO 1133 |
吸水率 | ISO 62 | ||
73°F, 24 hr | 0.80 | % | |
平衡, 73°F, 50% RH | 0.20 | % | |
硬度 | 額定值 | 單位制 | 測試方法 |
球壓硬度 (H 358/30) | 18900 | psi | ISO 2039-1 |
機(jī)械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 | 355000 | psi | ISO 527-2 |
拉伸應(yīng)力 (屈服) | 9140 | psi | ISO 527-2/50 |
拉伸應(yīng)變 (屈服) | 13 | % | ISO 527-2/50 |
斷張率 | 33 | % | ISO 527-2/50 |
拉伸蠕變模量 3 (1000 hr) | 189000 | psi | ISO 899-1 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強(qiáng)度 | ISO 179/1eA | ||
-22°F | 2.6 | ft·lb/in2 | |
73°F | 3.1 | ft·lb/in2 | |
簡支梁缺口沖擊強(qiáng)度 | ISO 179/1eU | ||
-22°F | 90 | ft·lb/in2 | |
73°F | 120 | ft·lb/in2 |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 (264 psi, 未退火) | 212 | °F | ISO 75-2/A |
熔融溫度 | 333 | °F | ISO 11357-3 |
線形膨脹系數(shù) - 流動 (73 到 131°F) | 0.000061 | in/in/°F | ISO 11359-2 |
Maximum Dynamic Service Temperature | 212 | °F |
電氣性能 | 額定值 | 單位制 | 測試方法 |
表面電阻率 | 1.0E+13 | ohm | IEC 60093 |
體積電阻率 | 1.0E+15 | ohm·cm | IEC 60093 |
相對電容率 (1 MHz) | 3.80 | IEC 60250 | |
耗散因數(shù) (1 MHz) | 0.0050 | IEC 60250 | |
漏電起痕指數(shù) (解決方案 A) | 600 | V | IEC 60112 |
可燃性 | 額定值 | 單位制 | 測試方法 |
UL 阻燃等級 (0.0630 in) | HB | UL 94 |
注射 | 額定值 | 單位制 | |
加工(熔體)溫度 | 374 到 446 | °F | |
模具溫度 | 140 到 212 | °F |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
POM 德國巴斯夫 N2320 0035(材料狀態(tài) )其它產(chǎn)品
POM 德國巴斯夫 N2320 0035(材料狀態(tài) )
POM 德國巴斯夫 H320(材料狀態(tài) )
POM 德國巴斯夫 H 2320 006 UNC Q600(材料狀態(tài) )