PPS 日本油墨 FZ-3600-L4
| 品牌名 | 出廠地 | 型號(hào) | 主要性能 | 提供商 | |
| PPS | 日本油墨 | FZ-3600-L4 | 玻璃/礦物，加工性良好 | 湘繡塑膠 |
| PPS 日本油墨 FZ-3600-L4 參數(shù)：比重2.0、絡(luò)氏硬度121、拉伸模量21000、抗張強(qiáng)度120、斷裂伸長(zhǎng)率0.8%、彎曲模量20000、彎曲強(qiáng)度175、缺口沖擊強(qiáng)度70、熱變形溫度265℃。 |
PPS 日本油墨 FZ-3600-L4 概述：
聚苯硫醚 PPS 英文名稱： Polyphenylene sulfide，簡(jiǎn)稱PPS。PPS is an excellent special engineering plastic a comprehensive performance. The dimensional stability of PPS has excellent resistance to high temperature, corrosion resistance, radiation resistance, flame retardant, balanced physical mechanical properties and excellent and excellent electrical performance characteristics, is widely used as structural materials, modified by filling, widely used in special engineering plastics. At the same time, also can be made into a film, various functional coatings and composites, and successfully applied in the electronic appliances, aerospace, automotive and transportation etc.. In recent years, the domestic enterprises to actively research and development, and initially formed a certain production capacity, change the past entirely dependent on imports of the situation. However, Chinese PPS technology has less product variety, high function products less urgent, capacity expansion and other issues, these will be the focus of development the next step of PPS
PPS 日本油墨 FZ-3600-L4
1.結(jié)構(gòu): 分子主鏈由苯環(huán)和硫原子交替排列構(gòu)成。主鏈中大量的苯環(huán)的存在使其分子剛硬，大量的硫醚鍵使分子主鏈又具有一定的柔順性。PPS分子結(jié)構(gòu)對(duì)稱，易于結(jié)晶，熱塑性PPS因有支鏈，破壞了分子結(jié)構(gòu)的對(duì)稱，故影響其結(jié)晶度，結(jié)晶度很小；熱固性PPS的結(jié)晶度較高，Tm為288℃。 PPS結(jié)構(gòu)對(duì)稱，無極性，吸水率低，故電絕緣性優(yōu)良。PPS中硫原子上的孤對(duì)電子使得PPS樹脂與玻纖、無機(jī)填料及金屬具有良好的親和性，使其易于制得各類增強(qiáng)復(fù)合材料及合金。
2. 性能：PPS是一種白色、結(jié)晶度高的聚合物，相對(duì)密度1.34，不燃。⑴ 力學(xué)性能：優(yōu)良，拉伸強(qiáng)度70 MPa ，彎曲強(qiáng)度67MPa，具有*的剛性和抗蠕變性，但其脆性較大，缺口沖擊強(qiáng)度較低。⑵ 熱性能：PPS的耐熱性十分優(yōu)異，其Tg為110℃，熔點(diǎn)286℃，負(fù)荷變形溫度為260℃，350℃以下的空氣中*穩(wěn)定，400℃空氣中短期穩(wěn)定，在氮?dú)庵?穩(wěn)定。此外PPS的阻燃性十分突出，是一般塑料所欠缺的。玻纖增強(qiáng)PPS的耐熱性更好，100℃時(shí)力學(xué)強(qiáng)度可保持初始值的80%，160℃時(shí)約60%，200℃時(shí)約40%。
⑶ 電性能：PPS結(jié)構(gòu)對(duì)稱，無極性，且吸水率低，故電絕緣性十分優(yōu)良，體積電阻率為4.5×1016Ω·cm，介電損耗很低，介電損耗角正切在較大范圍內(nèi)均保持很低的水平（103~106Hz時(shí)，僅為3.8×10-4），且受溫度、濕度影響不大。PPS常用于電器絕緣材料，其用量可占30%左右。
⑷ 耐化學(xué)藥品性：因其結(jié)晶度較高（60~80%），故具有良好的耐無機(jī)酸、堿、脂肪烴、芳香烴、酮、醇、氯代烴等性能，不溶于低于175℃的任何溶劑，其化學(xué)穩(wěn)定性接近于PTFE。
⑸ 其它性能：PPS具有優(yōu)良的耐候性，耐輻射性，對(duì)紫外線、鈷60射線及γ射線均穩(wěn)定。
PPS 日本油墨 FZ-3600-L4
應(yīng)用：
因?yàn)?/b>PPS材料有高熱變形溫度（HDT）和阻燃性能，并能充填長(zhǎng)而薄的截面，它的首要用途就是制造電氣連接件和電氣元件。對(duì)于一個(gè)電氣連接件來說，一般不需耐500°F的高溫，那為什么又需要高的熱變形溫度（HDT）呢？這里，連接件與印刷電路板之間的聯(lián)接加工方法是關(guān)鍵。隨著新團(tuán)結(jié)方法的使用，如紅外固結(jié)和汽相固結(jié)，材料所要經(jīng)受的實(shí)際溫度高達(dá)450°F，PPS在這么高的溫度下能保持其剛度，使插入的連接件的釘接觸面不至于松開。
由于元件趨向小型化，這就要求連接件材料能流動(dòng)較長(zhǎng)的距離，填充更薄的截面。一個(gè)連接件的間隔（連接件釘接觸面之間的間隔）一般中心距為 0．1英寸，并正在向 0．05英寸發(fā)展。流動(dòng)計(jì)百好的材料（如 PPS和液晶聚合物）將被考慮取代傳統(tǒng)的聚酯。由于絕緣塑料不應(yīng)該有容納或傳輸電行的能力，因此．材料中離
子含量（金屬含量）低就變得很重要了。降低PPS的離子含量已取得了進(jìn)展。
汽車工業(yè)是PPS的一個(gè)新市場(chǎng)。PPS用作汽車發(fā)動(dòng)機(jī)傳感器和鹵素?zé)糇€沒有用作主要部件。現(xiàn)在發(fā)動(dòng)機(jī)艙正在變小，而對(duì)發(fā)動(dòng)機(jī)性能要求卻越來越高。今后五年內(nèi)，汽車發(fā)動(dòng)機(jī)罩下的溫度將會(huì)高達(dá)340°F，到九十年代中期．會(huì)達(dá)到400°F以上。隨著發(fā)動(dòng)機(jī)溫度提高，與機(jī)油、燃料（汽油和甲醇）、防凍劑、傳導(dǎo)液、剎車液等接觸，對(duì)常用于機(jī)罩下的塑料來說是十分重要的問題。 PPS具有抗化學(xué)和耐高熱的優(yōu)點(diǎn)．正在被考慮用于燃料系統(tǒng)、導(dǎo)管和閥套。
已開發(fā)出可用作反光表面，如前燈和霧燈反光器的級(jí)PPS。這些牌號(hào)的材料可以耐鹵素?zé)舾哂?/b>400°F的溫度。而且同向熱膨脹性低，使燈在較寬的溫度范圍內(nèi)保持聚焦。PPS常被用作絕緣體（見上表）。然而，隨著一系列從抗靜電到導(dǎo)電的
PPS牌號(hào)的開發(fā)，許多問題也迎刃而解。例如，用作輸送可燃性流體的化學(xué)泵能聚集靜電荷，能產(chǎn)生火花，引起爆炸。抗靜電級(jí)PPS比普通級(jí)PPS具有更低的表面和體積電阻率，因此，用這種牌號(hào)的PPS做泵的 外殼可以接地以防止發(fā)生這類事故
導(dǎo)電PPS能隨電流升高而加熱至均勻溫度，可用于電阻加熱方面，如：柴油機(jī)燃料過濾器的預(yù)熱，汽車外鏡除霜，泵體自熱。PPS器具市場(chǎng)包括小型開關(guān)。加熱器內(nèi)殼、電機(jī)后罩、電刷架。使用PPS是利用它的高耐熱性和良好的電性能。PPS的耐化學(xué)性是它用于工業(yè)和機(jī)械市場(chǎng)的主要原因，這包括化學(xué)泵（內(nèi)殼和外殼）、閥門、管道配件、油田用部件和塔器填料
PPS 日本油墨 FZ-3600-L4 物性表：
| 性能項(xiàng)目 | 測(cè)試條件 | 測(cè)試方法 | 數(shù)值/描述 | 單位 | |
| 機(jī)械性能 | 拉伸強(qiáng)度（引張強(qiáng)度） | ASTM D638/ISO 527 | 130 | kg/cm2（MPa）[Lb/in2] | |
| 斷裂伸長(zhǎng)率 | ASTM D638/ISO 527 | % | |||
| 拉伸模量 | ASTM D638/ISO 527 | 18500 | kg/cm2（MPa）[Lb/in2] | ||
| 拉伸屈服伸長(zhǎng)率（延伸率） | ASTM D638/ISO 527 | % | |||
| 拉伸斷裂伸長(zhǎng)率（延伸率） | ASTM D638/ISO 527 | % | |||
| 彎曲模量（彎曲彈性率） | ASTM D790/ISO 178 | 17500 | kg/cm2（MPa）[Lb/in2] | ||
| 彎曲強(qiáng)度 | ASTM D790/ISO 178 | 200 | kg/cm2（MPa）[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | ||||
| IZOD 缺口沖擊強(qiáng)度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| Charpy沖擊強(qiáng)度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| 23℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| -30℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm（J/M）ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.96 | ||
| 成型收縮率 | ASTM D955 | % | |||
| 熔融指數(shù)（流動(dòng)系數(shù)） | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
| 熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | ℃（℉） | |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 維卡軟化點(diǎn) | ASTM D1525/ISO R306 | ℃（℉） | |||
| 熔點(diǎn) | - | ℃（℉） | |||
| 燃燒性（率） | UL94 | ||||
| 線性膨脹系數(shù) | ASTM D696/ISO 11359 | mm/mm.℃ | |||
| 電氣性能 | 介電常數(shù) | 100HZ | ASTM D150/IEC 60250 | ||
| 1MHZ | ASTM D150/IEC 60250 | ||||
| 體積電阻率 | ASTM D257/IEC 60093 | Ω.cm | |||
| 表面電阻率 | ASTM D257/IEC 60093 | Ω | |||
| 耐電弧性 | ISO 14782 | ||||
| 加工條件 | 干燥條件 | ||||
| 加工溫度 | 射嘴 | ℃ | |||
| 料筒前段 | ℃ | ||||
| 料筒中段 | ℃ | ||||
| 料筒后段 | ℃ | ||||
| 熔體溫度 | ℃ | ||||
| 模具溫度 | ℃ | ||||
| 壓力 | 注塑壓力 | Mpa | |||
| 保壓壓力 | Mpa | ||||
| 背壓 | Mpa | ||||
| 螺桿轉(zhuǎn)速 | rpm | ||||
| 其他 | 備注 | ||||
| 顏色 | |||||
| 特性 | |||||
| 用途 |
湘繡塑膠代理PPS系列產(chǎn)品：
湘繡提供：PPS日本寶理Polyplastics）6165A6玻璃\礦物增強(qiáng)材料 無鹵電氣/電子應(yīng)用領(lǐng)域UL阻燃VO,
湘繡提供：PPS日本寶理1140A6玻璃纖維增強(qiáng)材料, 40%高強(qiáng)度UL94阻燃VO,
湘繡提供：PPS日本寶理1140A64UL94,, 玻璃纖維增強(qiáng)材料, 40%阻燃VO
湘繡提供：PPS日本寶理1140A7玻璃纖維增強(qiáng)材料, 40%UL94,,阻燃VO
湘繡提供：PPS日本寶理6165A4填料/增強(qiáng)材料 玻璃\礦物無鹵用途 泵件工業(yè)領(lǐng)域UL94,,阻燃VO,5VA
湘繡提供：PPS日本寶理1150A64玻璃纖維\玻璃鱗片, 50% UL94阻燃VO,
湘繡提供：PPS日本寶理1140T11,玻璃纖維增強(qiáng)抗撞擊性，高汽車領(lǐng)域的應(yīng)用電氣/電子應(yīng)用領(lǐng)域UL 94阻燃V2
湘繡提供：PPS日本寶理1140A1玻璃纖維增強(qiáng)材料, 40%超高韌性UL94,,阻燃VO
湘繡提供：PPS日本寶理6465A62填料/增強(qiáng)材料玻璃\礦物, 60% UL94,,阻燃VO
湘繡提供：PPS日本寶理6345A4玻璃纖維增強(qiáng)材料, 30% PTFE潤(rùn)滑劑耐磨損性良好UL94,,阻燃VO
湘繡提供：PPS日本寶理2130A1碳纖維增強(qiáng)材料, 30%耐磨損性良好,導(dǎo)電UL94,,阻燃VO
湘繡提供：PPS日本東麗A604, A604X95 ,A604X97超高韌性玻璃纖維增強(qiáng)材料, 40% UL94,,阻燃VO
湘繡提供：PPS日本東麗（Toray Resin ）A310MX04填料/增強(qiáng)材料 玻璃\無機(jī)65%
湘繡提供：PPS日本東麗A503玻璃纖維增強(qiáng)材料, 30% UL94,,阻燃VO
湘繡提供：PPS日本東麗A310M剛性，高玻璃\無機(jī), 70% UL94,,阻燃VO。A305M,A400M
湘繡提供：PPS日本東麗A504X90玻璃纖維增強(qiáng)材料, 40%超高韌性高強(qiáng)度 UL94,,阻燃VO
湘繡提供：PPS日本東麗AR04-B玻璃纖維增強(qiáng)材料, 40% UL94,,阻燃VO
湘繡提供：PPS日本東麗A674M2增強(qiáng)材料, 40%抗撞擊性，高UL94,,阻燃VO
湘繡提供：PPS日本東麗AR10M-B增強(qiáng)材料玻璃\無機(jī), 65% UL94,,阻燃VO
湘繡提供：PPS日本東麗E604, A390M65, A310MX04,
湘繡提供：PPS 美國(guó)雪佛龍菲利浦（Ryton?）
湘繡提供：PPS 美國(guó)菲利浦R-4、玻璃纖維增強(qiáng)材料, 40%耐化學(xué)性良好，UL阻燃VO,5VA ，UL 746
湘繡提供：PPS 美國(guó)菲利浦R-4-02、玻璃纖維增強(qiáng)材料, 40%耐化學(xué)性良好,UL94,,阻燃VO,5VA
湘繡提供：PPS 美國(guó)菲利浦R-9-02玻璃纖維增強(qiáng)材料
湘繡提供：PPS 美國(guó)菲利浦R-4-200BL; 玻璃纖維增強(qiáng)材料, 40% 高強(qiáng)度黑色,UL94,阻燃VO,5VA
湘繡提供：PPS 美國(guó)菲利浦R-4-200NA, 玻璃纖維增強(qiáng)材料, 40% 高強(qiáng)度自然色UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-4-230BL, 玻璃纖維增強(qiáng)材料, 40% 可加工性，良好UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-4-230NA, 玻璃纖維增強(qiáng)材料, 40% 可加工性，良好UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-4XT, 玻璃纖維增強(qiáng)材料, 40%抗撞擊性，良好延展性UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-402XT玻璃纖維增強(qiáng)材料, 40%抗撞擊性，良好UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-7玻璃\礦物黑色UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-7-02玻璃\礦物黑色UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-4-230玻璃\礦物黑色UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-7-120BL玻璃\礦物黑色UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-7-120NA玻璃\礦物良好的強(qiáng)度UL94阻燃V0,5VA
湘繡提供：PPS 美國(guó)菲利浦R-7-220NA玻璃\礦物增強(qiáng)材料 良好的強(qiáng)度水解穩(wěn)定UL 94,阻燃VO
湘繡提供：PPS 美國(guó)菲利浦R-7-220BL,R-10-7006A玻璃\礦物水解穩(wěn)定黑色UL 94 V-0
湘繡提供：PPS 美國(guó)菲利浦R-7-121BL玻璃\礦物良好的強(qiáng)度黑色UL 94 V-0
湘繡提供：PPS 美國(guó)菲利浦R-7-121NA, 玻璃\礦物良好的強(qiáng)度 自然色UL 94 V-0,5VA
湘繡提供：PPS 美國(guó)菲利浦BR111玻璃\礦物,良好的電氣性能,良好的強(qiáng)度,自然色UL 94 V-0,
湘繡提供：PPS 美國(guó)菲利浦BR111BL玻璃\礦物,良好的電氣性能,良好的強(qiáng)度，黑色UL 94
PPS 日本油墨 FZ-3600-L4 加工方式：
（1）注塑：可采用通用注塑機(jī)，玻璃纖維增強(qiáng)PPS的熔融指數(shù)以50為宜。注塑的工藝條件為：料筒溫度，純PPS為280~330℃，40％GFPPS為300 -350℃；噴嘴溫度，純PPS為305℃，40％GFPPS為330℃；模具溫度120-180℃；注塑壓力，50-130 MPA。
（2）擠出：采用排氣式擠出機(jī)，工藝為：加料段溫度小于200℃；料筒溫度300-340℃，連接體溫度320-340℃，口模溫度300-320℃。
（3）模壓成型：適合大型制品，采用兩次壓縮，先冷卻，后熱壓。熱壓的預(yù)熱溫度純PPS為360℃左右15min,GFPPS為380℃左右20min;模壓壓力為10~30Mpa，冷卻到150℃脫模。
（4）噴涂成型：采用懸浮噴涂法和懸浮噴涂與干粉熱噴混合法，都是將PPS噴涂到金屬表面，再經(jīng)過塑化、淬火處理而得到涂層；PPS的涂層處理溫度在300℃以上，保溫30min。
日本寶理 PPS 應(yīng)用范圍：
（1）汽車工業(yè)：PPS用于汽車工業(yè)占45％左右，主要用于汽車功能件；如可代替金屬制作排氣筒循環(huán)閥及水泵葉輪，氣動(dòng)信號(hào)調(diào)解器等。
（2）電子電器：PPS用于電子電器工業(yè)可占30％，它適合于環(huán)境溫度高于200℃的高溫電器元件；可制造發(fā)電機(jī)和發(fā)動(dòng)機(jī)上的點(diǎn)涮、電涮托架、啟動(dòng)器線圈、屏蔽罩及葉片等；在電視機(jī)上，可用于高電壓外殼及插座、接線柱及端子板等；在電子工業(yè)、制造變壓器、阻流圈及繼電器的骨架和殼體，集成電路載體；利用高頻性能，制造H級(jí)繞線架和微調(diào)電容器等。
（3）機(jī)械工業(yè)：用于殼體、結(jié)構(gòu)件、耐磨件及密封材料，具體有泵體、閥門、軸承、軸承支架、活塞環(huán)及齒輪等。
樹脂廠商提供的PPS為一種相對(duì)質(zhì)量比較低（4000~5000）、結(jié)晶度較高（75%）的白色粉末，這種純PPS無法直接塑化成型，只能用于噴涂。用于塑化成型的PPS，必須進(jìn)行交聯(lián)改性處理，使熔體的粘度上升。一般交聯(lián)后的熔融指數(shù)達(dá)到10~20為宜；進(jìn)行玻璃纖維增強(qiáng)PPS的熔融指數(shù)可大一些，但不能大于200。
PPS的交聯(lián)方法有熱交聯(lián)和化學(xué)交聯(lián)兩種，目前以熱交聯(lián)為主。熱交聯(lián)的交聯(lián)溫度為150~350℃，低于150℃不發(fā)生交聯(lián)，高于350℃發(fā)生高度交聯(lián)，反而導(dǎo)致加工困難。
化學(xué)交聯(lián)需要加入交聯(lián)促進(jìn)劑，具體的品種有氧化鋅、氧化鉛、氧化鎂、氧化鈷等以及酚類化合物，六甲氧基甲基三聚氰酰胺、過氧化氫、堿金屬或堿土金屬的次氯酸鹽等。
PPS雖有交聯(lián)，但流動(dòng)性下降不多；因此，廢料可重復(fù)使用三次；PPS本身具有脫模性，可不必加入脫模劑；PPS經(jīng)過熱處理可提高結(jié)晶度及熱變形溫度，后處理的條件為：溫度204℃，時(shí)間30min。
PPS 日本油墨 FZ-3600-L4 ：
注明：本公司可支持多種原料混搭訂購(gòu),25公斤/包起訂（高價(jià)位的材料可以散賣），批量可折扣,款到發(fā)貨（周邊城市可貨到付款）.，提供售前咨詢，售后服務(wù)，并由專業(yè)工程師提供一對(duì)一的產(chǎn)品問題解決方案。 溫馨提示：因塑料行情波動(dòng)頻繁，網(wǎng)頁上的報(bào)價(jià)可能會(huì)與當(dāng)天實(shí)際報(bào)價(jià)有所差異，請(qǐng)用或直接詢價(jià)。若需要材料詳細(xì)物性資料及環(huán)保證書等，請(qǐng)我司工作人員索取。
:莫海波 （24小時(shí)）
：
: :6360906
:莫海波
:86
傳真號(hào)碼:86-
地址:廣東省東莞市常平大京九塑膠城
其它產(chǎn)品
PPS 日本油墨 FZ-3600-L3
PPS 日本油墨 FZ-3600-H5 BK
PPS 日本油墨 FZ-3600-D5
PPS 日本油墨 FZ-3600C1
PPS 日本油墨 FZ-3600
PPS 日本油墨 FZ-266D
PPS 日本油墨 FZ-2140-B2
PPS 日本油墨 FZ-2100 E1035
PPS 日本油墨 FZ-1140-K4