優勢說明:PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3詳細說明:
1.PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3
: 本公司可以免費提供各種材料認證
產品說明 | |
Vydyne® 909 Series are 25% glass fiber reinforced, ignition resistant Nylon 66 resins with UL 94V-0 flammability ratings. Available in natural and black color. Lubricated for machine feed and easy mold release. Vydyne 909 Series resins are modified with halogenated and other flame retardant additives to provide users with a product that meets Underwriters Laboratories (UL) 94V-0 flammability classifications down to thicknesses of 0.03 inches and 95-5VA thicknesses down to 0.06 inches. Vydyne 909 Series resins are designed for use in high performance applications requiring high rigidity and strength in addition to U.L. 94V-0 flammability classification. Vydyne 909 Series resins provide good toughness for high quality, crack-resistant molded parts, efficient regrind utilization, and good melting resistance to soldering operations. These properties make it a candidate to replace glass/FR polyesters and thermosets, such as phenolics or ureas, in many applications. Typical Applications/End Uses: The combination of 94V-0 fammability characteristics and high rigidity and strength makes Vydyne 909 Series resins ideal for appliance, electrical/electronic, and industrial applications. Typical applications include fire sprinkler system components, evision tuner parts and casings, electrical connectors, terminal strips/blocks, circuit board standoffs, circuit breakers, switch components, relays, coil forms, business machine/computer components and electrical spacers, rings, receptacles, and housings. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing (English)Technical Datasheet (English) |
UL 黃卡 2 | E70062-249072 |
搜索 UL 黃卡 | Ascend Performance Materials LLC.Vydyne® |
供貨地區 | 北美洲歐洲亞太地區 |
填料/增強材料 | 玻璃纖維增強材料, 25% 填料按重量 |
添加劑 | 鹵素潤滑劑 |
性能特點 | 剛性,高高強度經潤滑抗破裂性,良好鹵化韌性良好脫模性能良好阻燃 |
用途 | 電腦組件電氣/電子應用領域電器用具工業領域:連接器型號營業設備 |
機構評級 | FED L-P-410AMIL M-20693B |
RoHS 合規性 | RoHS 合規 |
UL 檔案號 | E70062 |
外觀 | 黑色自然色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
多點數據 | Isothermal Stress vs. Strain (ISO 11403-1) |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.47 | -- | g/cm3 | ISO 1183 |
收縮率 | ISO 294-4 | |||
橫向流量: 73°F, 0.0787 in | 1.0 | -- | % | |
流量: 73°F, 0.0787 in | 0.40 | -- | % | |
吸水率 | ISO 62 | |||
73°F, 24 hr | 0.70 | -- | % | |
平衡, 73°F, 50% RH | 1.5 | -- | % |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 1.32E+6 | 1.03E+6 | psi | ISO 527-2 |
拉伸應力 (斷裂, 73°F) | 19100 | 13100 | psi | ISO 527-2 |
拉伸應變 (斷裂, 73°F) | 2.2 | 3.0 | % | ISO 527-2 |
彎曲模量 (73°F) | 1.20E+6 | 725000 | psi | ISO 178 |
彎曲強度 (73°F) | 28000 | 20300 | psi | ISO 178 |
泊松比 | 0.37 | -- | ISO 527-2 | |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 4.5 | -- | ft·lb/in2 | |
73°F | 4.5 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 17 | -- | ft·lb/in2 | |
73°F | 19 | -- | ft·lb/in2 | |
懸壁梁缺口沖擊強度 (73°F) | 4.3 | -- | ft·lb/in2 | ISO 180 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 482 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 446 | -- | °F | ISO 75-2/A |
維卡軟化溫度 | 451 | -- | °F | ISO 306/B |
溶融溫度(DSC) | 482 | -- | °F | ISO 3146 |
線形膨脹系數 | ISO 11359-2 | |||
流動: 73 到 131°F, 0.0787 in | 1.1E-6 | -- | in/in/°F | |
橫向: 73 到 131°F, 0.0787 in | 5.6E-6 | -- | in/in/°F | |
RTI Elec | UL 746 | |||
0.0295 in | 266 | -- | °F | |
0.0591 in | 266 | -- | °F | |
0.118 in | 266 | -- | °F | |
RTI Imp | UL 746 | |||
0.0295 in | 149 | -- | °F | |
0.0591 in | 203 | -- | °F | |
0.118 in | 203 | -- | °F | |
RTI Str | UL 746 | |||
0.0295 in | 230 | -- | °F | |
0.0591 in | 230 | -- | °F | |
0.118 in | 230 | -- | °F |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 (0.118 in) | 1.0E+15 | -- | ohm·cm | IEC 60093 |
耐電強度 3 (73°F, 0.118 in) | 330 | -- | V/mil | IEC 60243-1 |
耐電弧性 (0.118 in) | PLC 6 | -- | ASTM D495 | |
相比耐漏電起痕指數(CTI) (0.118 in) | PLC 2 | -- | UL 746 | |
漏電起痕指數 (0.118 in) | 250 到 399 | -- | V | IEC 60112 |
高電弧燃燒指數(HAI) | UL 746 | |||
0.0295 in | PLC 0 | -- | ||
0.0591 in | PLC 0 | -- | ||
高電壓電弧起痕速率 (HVTR) (0.118 in) | PLC 4 | -- | UL 746 | |
熱絲引燃 (HWI) | UL 746 | |||
0.0295 in | PLC 0 | -- | ||
0.0591 in | PLC 0 | -- | ||
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
UL 阻燃等級 | UL 94 | |||
0.0150 in, All colors | V-0 | -- | ||
0.0295 in, All colors | V-0 | -- | ||
0.0591 in, All colors | V-05VA | -- | ||
0.118 in, All colors | V-05VA | -- | ||
灼熱絲易燃指數 | IEC 60695-2-12 | |||
0.0295 in | 1760 | -- | °F | |
0.0591 in | 1760 | -- | °F | |
0.118 in | 1760 | -- | °F | |
熱燈絲點火溫度 | IEC 60695-2-13 | |||
0.0295 in | 1380 | -- | °F | |
0.0591 in | 1380 | -- | °F | |
0.118 in | 1470 | -- | °F | |
極限氧指數 | 32 | -- | % | ASTM D2863 |
注射 | 干燥 | 單位制 | |
干燥溫度 | < 158 | °F | |
干燥時間 | 1.0 到 3.0 | hr | |
建議注入量 | 40 到 80 | % | |
建議的zui大回制料比例 | 25 | % | |
螺筒后部溫度 | 455 到 518 | °F | |
螺筒中部溫度 | 455 到 518 | °F | |
螺筒前部溫度 | 455 到 518 | °F | |
射嘴溫度 | 455 到 518 | °F | |
加工(熔體)溫度 | 491 到 518 | °F | |
模具溫度 | 68.0 到 194 | °F | |
注塑溫度 | 7980 到 20300 | psi | |
注射速度 | 快速 | ||
保壓 | 7980 到 20300 | psi | |
背壓 | 29.0 到 145 | psi | |
螺桿轉速 | 60 到 120 | rpm | |
合模力 | 1.9 到 4.5 | tons/in2 | |
墊層 | 0.118 到 0.252 | in | |
注射說明 | |||
Injection Time: <1 to 2.5 sec |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國首諾 909 玻璃纖維增強材料, 25% 填料按重量其它產品
PA66美國首諾 909 玻璃纖維增強材料, 25% 填料按重量
PA66美國首諾 909 電腦組件 電氣/電子應用領域 電器用具
PA66美國首諾 909 BK電腦組件 電氣/電子應用領域 電器用具
PA66美國首諾 909 BK抗破裂性,良好 鹵化 韌性良好
現貨PA66美國首諾 55HSP BK耐油性能熱穩定性 韌性良好
現貨PA66美國首諾 55HSP BK 耐化學性良好 耐磨蝕性,良好
現貨PA66美國首諾 55HSP BK 熱穩定 耐高溫 高韌性 黑色 增韌
現貨PA66美國首諾 55HSP BK 汽車應用:卡扣 套管 凸輪 軸承
PA66美國首諾 41LDC 剛性,高剛性,良好經潤滑
PA66美國首諾 20NSP工業領域: 緊固件 連接器