鋁焊絲OK AUTROD 5356
適用于焊接含約5% Mg不可時效硬化鋁合金和需要較高抗拉強度合金的實芯焊絲。 在海洋環境的抗腐蝕性。
鋁焊絲OK AUTROD 5754
分類: | ER5754, SFA/AWS A5.10, Wire Electrode, S Al 5754 (AlMg3), EN ISO 18273, Wire Electrode |
認證: | 04758, VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
Alloy Type: | AlMg |
焊縫金屬分析Typical Tensile Properties
As welded | ||
Elongation | Tensile Strength | Yield Strength |
23 % | 230 MPa | 110 MPa |
熔敷數據
安培 | 電壓 V | 直徑 |
60-170 A | 13-24 V | 0.8 mm |
60-170 A | 13-24 V | 0.9 mm |
90-210 A | 15-26 V | 1.0 mm |
140-260 A | 20-29 V | 1.2 mm |
190-350 A | 25-30 V | 1.6 mm |
鋁焊絲OK AUTROD 4043
| 分類: | ER4043, SFA/AWS A5.10, Wire Electrode, S Al 4043 (ALSi5), EN ISO 18273, Wire Electrode |
| 認證: | EN 13479, CE, 05794, VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
| Alloy Type: | ALSi5 |
焊縫金屬分析
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 18 % | 165 MPa | 55 MPa |
熔敷數據
| 安培 | 電壓 V | 直徑 |
| 90-210 A | 15-26 V | 1.0 mm |
| 140-260 A | 20-29 V | 1.2 mm |
| 190-350 A | 25-30 V | 1.6 mm |
| 280-400 A | 26-31 V | 2.4 mm |
鋁焊絲OK AUTROD 5556
適用于焊接含約5% Mg不可時效硬化鋁合金和需要較高抗拉強度合金的實芯焊絲。 在海洋環境的抗腐蝕性。
| 分類: | ER5556A, SFA/AWS A5.10, Wire Electrode, S Al 5556A (AlMg5Mn), EN ISO 18273, Wire Electrode |
| 認證: | EN 13479, CE, 05794, VdTüV |
| Alloy Type: | AlMgMn |
| As welded | |
| Impact Value | Testing Temperature |
| 24 J | 20 °C |
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 25 % | 295 MPa | 145 MPa |
熔敷數據
| 安培 | 電壓 V | 直徑 |
| 90-210 A | 15-26 V | 1.0 mm |
| 140-260 A | 20-29 V | 1.2 mm |
| 190-350 A | 25-30 V | 1.6 mm |
| 280-400 A | 26-31 V | 2.4 mm |
鋁焊絲OK AUTROD 5556
適用于焊接含約5% Mg不可時效硬化鋁合金和需要較高抗拉強度合金的實芯焊絲。 在海洋環境的抗腐蝕性。
| 分類: | ER5556A, SFA/AWS A5.10, Wire Electrode, S Al 5556A (AlMg5Mn), EN ISO 18273, Wire Electrode |
| 認證: | EN 13479, CE, 05794, VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
| Alloy Type: | AlMgMn |
焊縫金屬分析
夏比V型缺口沖擊性能
| As welded | |
| Impact Value | Testing Temperature |
| 24 J | 20 °C |
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 25 % | 295 MPa | 145 MPa |
熔敷數據
| 安培 | 電壓 V | 直徑 |
| 90-210 A | 15-26 V | 1.0 mm |
| 140-260 A | 20-29 V | 1.2 mm |
| 190-350 A | 25-30 V | 1.6 mm |
| 280-400 A | 26-31 V | 2.4 mm |
鋁焊絲OK AUTROD 5554
OK Autrod 5554是一種含2.7% Mg的實芯鋁焊絲。該焊絲推薦用于焊接諸如5454之類的鋁鎂合金。典型應用包括化學品儲罐、車輪和車架部件等汽車零件。其焊縫金屬在高溫條件下不易發生應力腐蝕開裂。
| 分類: | ER5554, SFA/AWS A5.10, Wire Electrode, S Al 5554 (AlMg2,7Mn), EN ISO 18273, Wire Electrode |
| 認證: | EN 13479, CE, A5.10/A5.10:2012 ER5554, CWB |
Approvals are based on factory location. Please contact ESAB for more information.
| Alloy Type: | AlMg 2.7Mn |
焊縫金屬分析
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 17 % | 230 MPa | 110 MPa |
熔敷數據
| 安培 | 電壓 V | 直徑 |
| 140-260 A | 20-29 V | 1.2 mm |
| 190-350 A | 25-30 V | 1.6 mm |
鋁焊絲OK AUTROD 5087
適用于焊接含5% Mg的鋁合金和需要達到較高抗拉強度合金的實芯焊絲。合金化元素Zr在硬化凝固過程中具有優良的抗熱裂紋作用。
| 分類: | ER5087, SFA/AWS A5.10, Wire Electrode, S Al 5087 (AlMg4,5MnZr), EN ISO 18273, Wire Electrode |
| 認證: | EN 13479, CE, 61.039.07, DB, 05816, VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
| Alloy Type: | AlMgMn |
焊縫金屬分析
夏比V型缺口沖擊性能
| As welded | |
| Impact Value | Testing Temperature |
| 35 J | 20 °C |
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 30 % | 280 MPa | 130 MPa |
熔敷數據
| 安培 | 電壓 V | 直徑 |
| 90-210 A | 15-26 V | 1.0 mm |
| 140-260 A | 20-29 V | 1.2 mm |
| 190-350 A | 25-30 V | 1.6 mm |